2.2.2 Butt weld
bend test specimens are to be tested at ambient temperature and are
to be bent through an angle of 120° over a former having a diameter
which relates to the thickness of the test specimen as detailed in
subsequent Sections. For each pair of bend test specimens, one specimen
is to be tested with the face of the weld in tension and the other
with the root of the weld in tension.
2.2.3 Macro examinations
are to be carried out on polished and etched specimens at a maximum
magnification not exceeding x10. The examination is to ensure complete
fusion, inter-run penetration and freedom of defects.